PCE-5000 is a Ultrasonic testing device that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

PCE-FD 20 is a Ultrasonic testing device or ultrasonic thickness gauge with a large LCD screen that displays A-scan maps of ultrasonic signals as well as B-scan cross sections. Ideal for use in mechanical engineering, aerospace and metallurgical applications, this high-frequency ultrasound-based thickness meter uses a contact transducer (two different probes included; 45° and 90°) to measure material thickness and identify flaws and defects such as discontinuity in welds.

• Operating frequency range: 1 … 10 MHz
• Measured time interval range: 6 … 1000 microseconds (µs)
• Sound velocity: 1000 … 9999 m/s 

• Working frequency: 40 kHz (± 2 kHz)
• Operating time: >10 hours
• Various attachments
• Color display: 3.5" touch panel TFT
• Soundproof headphones

The Ultrasonic testing device has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces.

• Probe is 50 Newtons / 11.2 lbf force, 10 and 98 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting

The Ultrasonic testing device has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces and nitrided surfaces.

• Probe is 10 Newtons / 2.2 lbf force, 50 and 98 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting 

The Ultrasonic testing device has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces and nitrided surfaces.

• Probe is 98 Newtons / 22 lbf force, 10 and 50 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting